It depends on what type of polymer you're trying to simulate. For brittle polymers, LEFM should be able to work. While for many ductile polymers, elastic-plastic fracture mechanics should be used.
PE has significant plasticity compared with most metals. Basically, fracture is impossible when plasticity is too huge, only necking occurs. What is the service condition of your LLDPE?
It depends on what type of
It depends on what type of polymer you're trying to simulate. For brittle polymers, LEFM should be able to work. While for many ductile polymers, elastic-plastic fracture mechanics should be used.
Iam presently working on
Iam presently working on LLDPE.
Can you please berif on what are the major changes from fracture in metals
PE has significant
PE has significant plasticity compared with most metals. Basically, fracture is impossible when plasticity is too huge, only necking occurs. What is the service condition of your LLDPE?
It is used to analsys the
It is used to analsys the fracture toughness when used in automobile fuel tanks.