Shape memory alloy material models including plasticity implemented in ABAQUS
I am working with shape memory alloys (nitinol), and am in that respect investigating fracture behaviour of NiTi, using, among other things, simulations in ABAQUS. ABAQUS doesn't have a material model that include plasticity unless you pay for it. I am wondering if anyone have implemented either of the following models as a UMAT, and if you are willing to share the code with me.
The models I am interested in are:
- Yan et al. (2003): based on Auricchio's model with a slight change in the martensite evolution and including plasticity (basic J2-flow theory)
- Wang X.M. (2008): a micromechanical approach to phase transformation, accounting for plasticity effects through crystal plasticity (this I am particularly interested in).
- Lagoudas et al. (2004): this approach is directed towards transformation induced plasticity
I would be very thankful to anyone who can help me out. If someone has implemented other material models which include shape memory behaviour and plasticity I would be very interested in this too.
Jim
- Jim S. Olsen's blog
- Log in or register to post comments
- 25171 reads
Comments
There is a UMAT with plasticity for NiTi
Contact Dr. Nuno Rebelo at Simulia West for details.
Xiao-Yan Gong, PhD President Medical Implant Mechanics LLC 26895 Aliso Creek Road, Suite #B716 Aliso Viejo, CA 92656
Modeling of SMA in Patran and marc.
I am doing my Masters degree,project is on Shape memory alloy(NITINOL)......does any body know how to model SMA using Patran and MSC.Marc?????
Modeling of SMA in Patran and MSC.MARC (Nitinol, Shape Memory)
T.Kim Parnell, PhD,PE
Sunnyvale, CA
http://www.linkedin.com/in/parnellpec
MSC.MARC has excellent capabilities for modeling of Shape Memory Alloys (SMA) like Nitinol (NiTi, Nickel Titanium). MARC has 2 models:
The Thermo-Mechanical Shape Memory Model may be used directly for modeling things like shape recovery. It includes the Superelastic response as a subset.
More details, full documentation, etc. are available in the MSC.MARC documentation that you can find on http://www.ScribD.com The MSC Software VPD Forums are another good source of detailed information.
There is a nice video showing a coupled Electrical-Joule Heating-Mechanical analysis of a Shape Memory Alloy actuator (using the Thermo-Mechanical Shape Memory Model) and a STent-Artery interaction (using the Mechanical Shape Memory Model) from Sean Harvey and presented at SMST-2010 posted in HD at:
http://www.youtube.com/watch?v=22OBH3M1oYE
or at
http://slidesha.re/acw9BT
Regards,
Kim
Plasticity of Nitinol
Hi everyone,
I am a student, nice to meet you all here,
I am studying in Abaqus with the problem is that simulation the compression test of medical device with Nitinol material.
I already know how to simulate, but the result of simulation (deformation) is quite small in comparison with experiment result. I think this is because of my mistake in the input value of plasticity for Nitinol. In this case, I declare only the elasticity.
Therefore, I would like to ask you about the plasticity information in order to define Nitinol material properties.
Thanks all of you for your sharing,
Nitinol
Hello
What model do you use ? Do you have a subroutine code ?
Are you aware that there is a built-in model ?
Log on to the support page
http://simulia.custhelp.com/cgi-bin/abaqus.cfg/php/enduser/home.php
and create a free user account.
Then search for
answer ID 1658: UMAT and VUMAT routines for the elastic-plastic simulation of Nitinol
answer ID 4699: Abaqus/CAE plug-in utility to calibrate Nitinol material behavior
Good luck
Frank
------------------------------------------
Ruhr-University
Bochum
Germany
SMA modeling
Dear Frank, with a free account it seems that i Cannot visualize the answers that you suggested... I am a completely new abaqus user and i would need a SMA model that simulates the shape memory effect and that includes plasticity... Could you help me? Are there some clear tutorials or some other discussions somewhere for the SMA rutines and the materiale calibration? Thanks a lot!
Fabrizio