Exponential model W (strain energy density function)- Zero stress zero strain condition
Hi,
I am new here and have a very basic question on the Strain Energy Density (SED) function of exponential model.
This is the exponential model SED form : W=a(e(b(I1-3))-1)
Now we have certain postulates such as that
1.W=0 when there is no deformation and
2. stress=0 when strain =0.
When there is no deformation I1=3 and hence W=0, which is correct.
However, when we take the 1st derivative of W with respect to I1 to get our stress and then substitute I1=3 we don't get stress=0.
I know this is a standard model used very often, so I am obviously wrong in my understanding of how the 2nd postulate works for SED functions.
Can some one clarify as to how to work the 2nd postulate (stress=0 when strain=0) for this particular constitutive model ?
N
- maverick_269's blog
- Log in or register to post comments
- 17499 reads
![Subscribe to Comments for "Exponential model W (strain energy density function)- Zero stress zero strain condition"](https://imechanica.org/misc/feed.png)
Comments
What is derevative of W
What is derevative of W with respect to I1?
Stresses is derevative of W with respect strains.
Re. exponential strain energy density function
The strain energy density function is:
.
. The derivative of W wrt I1 is
and from Wiki Tensor derivatives
. Hence the stress is not-zero at zero strain. Your model is not hyperelastic.
From Wiki Hyperelastic material we see that
A better model is
which is similar to Fung's exponential model and does give zero stress at zero strain.
Thank you
You consider the incompressible material. In this case we have hydrostatic pressure which is not determined by strains.
If I understand right then for Fung material sresses is not zero under simplification for big stretches.
Re: Fung material and undetermined mean stress
The model and equations discussed in this blog describes isochoric deformations. The stress computed using these equations may not be able to balance the applied external forces. The unbalanced forces will have to be balanced by the mean stress (p). In other words, the mean stress will depend on the applied external forces in such a way that internal and external forces are balanced.
At zero strain the external force is (presumably) zero and hence the pressure predicted by the Fung model will be zero.
-- Biswajit
Undetermined mean stress
Yes, typically the pressure field will have to be solved for separately in order to satisfy equilibrium and boundary conditions. This is one of the blessings and curses of being literal about incompressibility.
Matt Lewis
Los Alamos, New Mexico
Null
Null
How is the proposed model better than the initial one?
Thanks for the explanation.
Is'nt it possible that W could still be zero based on what value our lagrange multiplier p might turn out to be say in an uniaxial condition?
But I don't understand as to how is the proposed one any different from the initial one I mentioned in my post W=a[exp[b(I1-3)]-1]
And a follow up question would be as to what will happen if such models are used to fit our experimental data? It would still be able to get the constants, so my qn is as to what is the implication of using such models to fit our experimental data?
Re: Incompressible hyperelasticity and exponential models
Consider a ball made of an incompressible solid. Apply a uniform external pressure to the ball. Under this condition the ball is effectively rigid and does not have any internal energy. What is the stress in the ball?
Hyperelasticity is a model for material behavior. Such models should be independent of external forces, body forces, and other boundary conditions. Your model depends on the boundary conditions for predicting the expected elastic response. The modified model does not. Both models are less than realistic. That is why we prefer to use compressible hyperelastic models when possible.
-- Biswajit
Re: Incompressible hyperelasticity and exponential models
Mathematically if there is no stored energy then the stress should be zero as well for a hyperelastic material. So for the example you have given also this will hold good right?
However, I still don't quite understand how the modified model response function will make the stress=0 when strain =0.
So according to the modified equation, we have
so
, so still we donot satisfy the stress=0, when strain=0 condition here. What am i missing here?
mathematically our
∂W/(∂I_1 )=-4abe^(b〖(I_1-3)〗^2 ) and we know that
Considering that we do not need the p to be solved to get our zero-stress-strain configuration..
More on exponential hyperelasticity
A good way to understand incompressible behavior in rubbers is to start with the ball image and vary boundary conditions. In the previous example you could substitute the applied pressue with zero pressure and not observe any change. Now take the ball and put it between two perfectly smooth plates and apply a clamping force on the plates. That is equivalent to having a slightly more complex pressure boundary condition on the ball. What is the stress in the ball? And so on.
Regarding the formula above see http://www.wolframalpha.com/input/?i=A+%28exp%28b%28x-3%29^2%29-1%29
-- BIswajit
Thanks Dr.Biswajit
I understand now, I think.
Can you please provide me with any book references that discuss this concept of zero stress-zero strain with an example like you have said to better understand how this works for the various phenomenological models that exist out in the literature?
Regards
Nisha
Thank you
Thank you